White Zirconium Ceramic Beads With Acid Resistance 1000-1300Mpa Compressive Strength
| Bulk Density: | 3.6-3.8 G/cm3 |
|---|---|
| Hardness: | 8.5-9.5 Mohs |
| Acid Resistance: | Excellent |
8.5-9.5 Mohs Zirconia Mill Beads with Excellent Chemical Resistance
| Compressive Strength: | 1000-1300Mpa |
|---|---|
| Shape: | Cylindrical |
| Heat Resistance: | >1300℃ |
White Zirconia Mill Beads 1000-1300Mpa Heat Resistance >1300℃
| Bulk Density: | 3.6-3.8 G/cm3 |
|---|---|
| Color: | White |
| Chemical Resistance: | Excellent |
Zirconia Cylindrical High Chrome Steel Grinding Media Balls
| Chemical Resistance: | Excellent |
|---|---|
| Heat Resistance: | >1300℃ |
| Acid Resistance: | Excellent |
Industrial White Ceramic Blasting Media Material Ceramic Specific Gravity 2.6-2.8
| Melting Point: | 2050°C |
|---|---|
| Material: | Ceramic |
| Shape: | Irregular |
1700°F Al2O3 Ceramic Bead Blasting For Industrial Surface Treatment
| Refractoriness: | 1790°C |
|---|---|
| Hardness: | 7.5-8.5 |
| Specific Gravity: | 2.6-2.8 |
Alumina Oxide Ceramic Blasting Media with 1700°F Maximum Operating Temperature
| Shape: | Irregular |
|---|---|
| Refractoriness: | 1790°C |
| Maximum Operating Temperature: | 1700°F |
Irregular Shape Silicon Carbide Ceramic Parts With Melting Point Of 2050°C
| Abrasive Grain: | Alumina Oxide |
|---|---|
| Hardness: | 7.5-8.5 |
| Material: | Ceramic |
3.85g/Cm3 Ceramic Grinding Beads B205 Zirconium Silicate Beads
| Main Chemical: | 65% ZrO2, 35% SiO2 |
|---|---|
| Vicker Hardness: | ≥700HV |
| Density: | 3.85g/Cm3 |
Z300 Solid White Ceramic Balls 30%~35% Sio2 High Sphericity Smooth
| Usage: | Industry |
|---|---|
| Type: | Z300 |
| Hardness: | 7-8Mohs |